فایل ورد Microstructure and magnetic properties of La–Zn substituted Y-type hexaferrite synthesized by sol-gel autocombustion method

لینک دانلود

 فایل ورد Microstructure and magnetic properties of La–Zn substituted Y-type hexaferrite synthesized by sol-gel autocombustion method دارای 12 صفحه می باشد و دارای تنظیمات در microsoft word می باشد و آماده پرینت یا چاپ است

فایل ورد فایل ورد Microstructure and magnetic properties of La–Zn substituted Y-type hexaferrite synthesized by sol-gel autocombustion method  کاملا فرمت بندی و تنظیم شده در استاندارد دانشگاه  و مراکز دولتی می باشد.

توجه : در صورت  مشاهده  بهم ريختگي احتمالي در متون زير ،دليل ان کپي کردن اين مطالب از داخل فایل ورد مي باشد و در فايل اصلي فایل ورد Microstructure and magnetic properties of La–Zn substituted Y-type hexaferrite synthesized by sol-gel autocombustion method،به هيچ وجه بهم ريختگي وجود ندارد


بخشی از متن فایل ورد Microstructure and magnetic properties of La–Zn substituted Y-type hexaferrite synthesized by sol-gel autocombustion method :


سال انتشار : 1395

نام کنفرانس یا همایش : دهمين همايش مشترک و پنجمين کنفرانس بين المللي انجمن مهندسي مواد و متالورژي و انجمن علمي ريخته گري ايران

تعداد صفحات :12

چکیده مقاله:

In present study, Y-type hexaferrite Sr2-xLaxNi2Fe12-xZفایل ورد Microstructure and magnetic properties of La–Zn substituted Y-type hexaferrite synthesized by sol-gel autocombustion methodO22 (x = 0.0, 0.1, 0.2, 0.3, 0.4 and 0.5) nanoparticle prepared by sol-gel auto-combustion method. All of the samples calcined at1000 °C for 3h. X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and vibrating sample magnetometer (VSM) were used to investigate the specimen’s properties. XRD patterns confirm that the prepared specimens at 1000 were Y-type hexaferrite single phase. FESEM micrograph showed that all of the particles had a hexagonal platelet shape and with the increase of La3+ – Zn2+ contents, the size of particles reduced. Thisreduction is relative on the inhibitor properties of additional rare earth element. The VSMmeasurements were used to determine the saturation magnetization (Ms), remanent magnetization (Mr) and coercivity (Hc) of the samples. This results showed that by increasingthe La3+ and Zn2+ contents, the saturation magnetization and remanent magnetization wereincreased from 37.94 to 44.14 emu/g and 18.46 to 20.56 emu/g, respectively, whereas coercivity was decreased from 1199.95 to 898.6 Oe. Magnetic properties revealed that this material is suitable for high frequency applications, such as electromagnetic devices, because of its soft magnetic properties.